ISOTHANE TPU樹脂:

創新高性能、高附加價值之綠色環保材料
   大東樹脂掌握關鍵技術，自行研發的高性能熱塑型聚氨酯彈性體，簡稱TPU樹脂，為高級環保材料，可於土中自然分解，是優異的環保材料。具備耐磨損、耐撕裂、及耐低溫曲折等特性。大東樹脂TPU樹脂系統發展完整，分為芳香族與脂肪族兩大類。
  未來輕量化與節能減碳的趨勢，也成功推出以塑代鋼的熱塑性長纖維增強複合材料及客製化規格的樹脂與複合材料等。
  大東樹脂推出的長纖維增強複合材料(LFRT)具有優異的剛性強度及耐衝擊特性，可取代工業零部件的金屬材料，有效減輕產品重量，且成型品表面具有良好光澤度及平滑性，耐磨耗性及尺寸安定性也較一般複合材料更佳。
  塑化產品生產線全程使用電腦自動化程序控制，採用先進的雙軸反應押出設備產製高性能材料，並透過精密檢驗儀器之檢測及自動化設備之包裝堆棧，確保成品外觀及儲存品質。

ISOTHANE 5000系列 - 生醫級

項目名稱	聚醚型 TPU 樹脂生醫級
產品特性	優異耐水解性、生物相容性、抗菌性、耐低溫性適用於射出、吹膜以及押出等用途。
應用場合	醫療導管、醫療管材等相關醫療用品，符合USP Class VI。

項目名稱	聚醚型 TPU 樹脂生醫級
Description	ISOTHANE 5000 series products are polyether based thermoplastic polyurethanes. They exhibit excellent bio-compatibility, hydrolytic resistance, fungus resistance, and low temperature performance properties. These products can be injection molded, blow molded, and extruded.
Supply and Storage	ISOTHANE TPU resins are supplied in pellet form packed in 25kg moisture proof bags. All TPU resins have been dried before packing. ISOTHANE TPU resins should be stored in cool and dry environment in their original containers until be used. Storage temperature should not exceed 30°C. If only a portion of TPU resins was used from a bag, the remainder of TPU resins should be tightly closed.
Drying	TPU resins are hygroscopic and pre-drying of TPU resins is always a necessary step before processing. Depend on the climate, the granule exposed to the atmosphere will absorb moisture very quickly. The moisture might bring about partial degradation of polymers and the formation of bubbles or streaks in the molded and extruded parts. In order to ensure the efficient and successful processing into quality parts, the moisture content in TPU resins is recommended less than 0.02%. A desiccant-bed-type hopper dryer is recommended for drying ISOTHANE 5000 series. The dew point of the inlet air should be in the range of -30 to -40°C. About the recommended drying conditions, please view ISOTHANE individual data sheets.
Processing - Extrusion	Barrel and Motor High torque drive capacity at low speed Vented or standard barrels acceptable Screw Compression ratios between 2:1 and 3:1 Minimum L/D of 30/1 Feed Throat Vertical and tangential Water cooling is recommended Screen Pack Streamlined breaker plates with screen packing is recommended Typical 40/80/80/40 mesh screens Die Streamline with good temperature control Land Length is generally 10 to 15 times the part thickness Coat-hanger manifold-type dies are recommended for extruding film and sheet Crosshead dies are recommended for wire, cable and hose jacketing Side-fed rotating dies are recommended for blown film About the recommended extrusion temperatures, please view ISOTHANE individual data sheets.
Processing - Injection Molding	Barrel and Motor High torque drive capacity at low speed Vented or standard barrels acceptable Screw Compression ratios between 2:1 and 3:1 Metering screw with gradual transition zone Injection Pressure Typical 6,000 to 15,000 psi Hold pressure 60 – 70% of forward time Injection speed Slow to moderate Depends on gating, wall section and flow length About the recommended injection molding temperatures, please view ISOTHANE individual data sheets.
Coloring	Generally, ISOTHANE TPU resins are supplied in their natural color. They can be colored by blending with pigment or pigment master batch. Using master batch based on TPU is recommended. Other master batch based on polyethylene or polystyrene is suitable to a limited extent. All colorants employed in TPU resins must be pre-dried before processing. The normal addition of pigment or pigment master batch is 0.2%-0.5% or 1-3%.
Additives	Various additives can be used to enhanced the properties of ISOTHANE TPU resins, e.g. anti-blocking agents, antioxidant, UV stabilizers or release agents. Most additives supplied as master batches are available. But not all additives are compatible with ISOTHANE TPU resins. It is recommended to inquire of your suppliers or our technical service before compounding.
Recycling	For ISOTHANE TPU resins, up to 20% of regrind may be recycled with virgin material depending on finished parts requirements. The regrind material has to be kept free of contamination, diced and dried before re-using. The material which has been contaminated, discolored or degraded is not suitable for recycling. TPU resins may decrease desired properties, e.g. hardness and mechanical properties, due to improperly mixing with regrind. Regulatory or testing organizations (e.g., UL) may have specific requirements limiting the allowance amount of regrind. Certain quality requirements laid down in specifications may exclude the use of regrind material.
Healthy and Safety Information	Before working with these products, it is essential that all operators are aware of the healthy and safety precautions. ISOTHANE TPU resins can be processed or machined over a wide range of temperature. There can be some smoke formation during processing. The smoke that contains some decomposition substances of TPU or additives may cause irritation to human body. Generally, the temperature does not exceed 240°C that can reduce decomposition formation. An effective extraction system, especially in the melt outlet zone, is necessary. The detail information concerning healthy and safety can be available in safety data sheets (SDS) or contact our technical service.
Disposal	ISOTHANE TPU resins present no hazard to the environment or water. They can be dumped on municipal landfill or in a waste incineration plant. The official regulations on waste disposal should be observed.

項目	Units	ASTM	5075A	5080A	5085A	5090A	5095A
比重		D-792	1.10	1.12	1.13	1.13	1.15
硬度	Shore A	D-2240	75A	82A	85A	90A	95A
抗張强度	MPa psi	D-412	31 4500	37 5300	39 5600	41 6000	51 7300
@ 50% 延伸率	MPa psi	D-412	2.3 340	3.6 520	3.9 560	6.2 900	15 2180
@ 100% 延伸率	MPa psi		3.2 460	5.4 780	5.9 850	8.3 1200	19 2820
@ 300% 延伸率	MPa psi		5.9 850	10 1500	12 1800	17 2400	36 5240
斷裂延伸率	%	D-412	650	620	540	550	438
撕裂强度	N/mm lb/in	D-624 DIE C	70 400	80 450	90 500	120 700	190 1060
彎曲模數	MPa psi	D-792	29 4140	35 5050	43 6200	72 10400	96 14000

項目	Units	ASTM	5055D	5065D	5075D	8101-B	8102-B
比重		D-792	1.17	1.17	1.18	1.20	1.18
硬度	Shore D	D-2240	57D	65D	74D	80D	76D
抗張强度	MPa psi	D-412	51 7340	53 7670	54 7760	75 11000	60 8700
@ 50% 延伸率	MPa psi	D-412	25 3610	35 5030	46 6640	1480 214000	1080 156000
@ 100% 延伸率	MPa psi		31 4490	40 5790	46 6740
@ 300% 延伸率	MPa psi		48 6980	49 7110	52 7540
斷裂延伸率	%	D-412	400	340	322	125	150
撕裂强度	N/mm lb/in	D-624 DIE C	225 1280	270 1540	370 2100	-	-
彎曲模數	MPa psi	D-792	134 19500	420 60800	1360 197000	1730 250000	1370 198000

上表所列數據資料僅供參考

ISOTHANE聚醚型TPU樹脂 5000系列生醫级

適用在醫療導管、醫療管材和醫療用品，符合USP Class VI.